Tapered implantable device and methods for making such devices

ABSTRACT

A tapered implantable device includes an ePTFE tubular member having a tapered length portion. The tapered length portion provides rapid recovery properties. The tapered length portion can feature a microstructure that includes a multiplicity of bent fibrils.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. patent application Ser. No. 15/786,670, filed Oct. 18, 2017, which is a continuation of U.S. patent application Ser. No. 14/557,927, filed Dec. 2, 2014, which claims the benefit of U.S. Provisional Application No. 61/912,339, filed Dec. 5, 2013, all of which are incorporated herein by reference in their entireties for all purposes.

TECHNICAL FIELD

This document relates to tapered implantable devices and methods for making such devices that may be used for providing a lumen for fluid flow in bodily cavities, organs, and vessels within a patient.

BACKGROUND

Medical devices are frequently used to treat the anatomy of patients. Such devices can be permanently or semi-permanently implanted in the anatomy to provide treatment to the patient. Frequently, these devices, including stents, grafts, stent-grafts, filters, valves, occluders, markers, mapping devices, therapeutic agent delivery devices, prostheses, pumps, bandages, and other endoluminal and implantable devices, are inserted into the body at an insertion point and delivered to a treatment site.

Devices such as grafts and stent-grafts are used in a variety of places in the human body to repair, support, and/or replace anatomical lumens, such as blood vessels, respiratory ducts, gastrointestinal ducts, and the like. Such devices can, for example, provide lumens for fluid flow. In such configurations, flexible and durable devices are needed.

In various applications, such as particular vascular applications, it is desirable to utilize a graft or artificial lumen having a tapered length portion. Tapered length portion and/or grafts may also be useful in connecting discreet grafts or tubes of differing diameters. As such, there is an ongoing need to provide tapered implantable devices, such as grafts and/or stent-grafts, which have improved flexibility and/or rapid recovery properties. Such devices may improve characteristics of the blood flow of a patient and reduce thrombosis.

SUMMARY

In a first general aspect, a tapered implantable device for repairing or replacing a lumen in the body of a patient comprises a tubular member, such as an ePTFE tubular member, having a tapered portion. The tapered portion includes a multiplicity of substantially bent fibrils, providing a region having rapid recovery properties.

In various implementations, a tapered implantable device in accordance with the present disclosure is formed by stretching a smaller diameter polymeric tubular member over a first mandrel having larger and smaller opposing ends and an intermediate tapered length segment to create a first tapered length portion on the polymeric tubular mandrel. The tubular member is then longitudinally compressed on a second mandrel to form the tapered implantable device by converting the first tapered length portion into a second tapered length portion having a multiplicity of bent fibrils. The tapered implantable device is then removed from the second mandrel and prepared for implantation into the anatomy of a patient.

The details of one or more embodiments are set forth in the accompanying drawings and the description below. Other features, objects, and advantages will be apparent from the description and the drawings, and from the claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side view of a portion of a tapered implantable device in accordance with the present disclosure;

FIG. 2 is a schematic representation of a microstructure of ePTFE material in accordance with the present disclosure;

FIG. 3A is a side view of a first tapered mandrel, and FIG. 3B is a side view of a tapered implantable device in a stage of formation; and

FIG. 4A is a side view of a second tapered mandrel, FIG. 4B is a side view of a tapered implantable device in another stage of formation, and FIG. 4C is a side view of a second tapered mandrel and complimentary female die.

Like reference symbols in the various drawings indicate like elements. It should also be noted that the accompanying drawing figures referred to herein are not all drawn to scale, but may be exaggerated to illustrate various aspects of the present disclosure, and in that regard, the drawing figures should not be construed as limiting.

DETAILED DESCRIPTION OF THE ILLUSTRATED EMBODIMENTS

This document describes devices, systems, and methods that are useful, for example, for repairing, supporting, and/or replacing anatomical lumens. Several implantable medical devices are described herein, and in general any of the features described with respect to a particular device may also be used with any of the other devices described herein. In some examples, one or more features described with respect to a particular device may be added to or included with another device. Also, various combinations or sub-combinations of any of the features described herein may generally be used with any of the devices described herein.

In general, any of the implantable devices described herein can be delivered to, and deployed at, an in vivo deployment site within a body of a patient using various minimally invasive surgical techniques. Likewise, these devices may also be surgically implanted via vascular surgical techniques.

Further, any of the implantable medical devices described herein can be delivered to, and deployed at, an in vivo deployment site within a body of a patient using various minimally invasive transcatheter deployment techniques.

Any of the implantable medical devices discussed herein can be used to repair, replace, and/or provide support to a body lumen. In various embodiments, implantable medical devices of the present disclosure can be used in a body lumen, including those within the circulatory and gastrointestinal systems.

As used herein, “implantable” means implanted in the body of a patient for more than 29 days.

As used herein, “taper” or “tapered” generally refers to a region of transition from one portion of a device to another portion of the same device. Most typically, a taper transitions a portion of a tubular device having a circular transverse cross-section with a larger inside diameter to another portion of the same device having a circular transverse cross-section with a smaller inner diameter. The region can be symmetrically or asymmetrically conical, or may be shaped to include bumps, reversals, or flares.

For the sake of consistency and clarity, the term “portion” is used to identify a length of, for example, a tubular member. The term “segment” is used to identify a length of, for example, a first or second mandrel. These terms are not intended to be limiting, and are chosen primarily to assist in understanding the references to various tubular members and mandrels.

FIG. 1 illustrates an example tapered implantable device 100 comprising a polymeric tubular member 102 having a first smaller diameter length portion 104, a second larger diameter length portion 106, and a tapered length portion 108. Polymeric tubular member 102 can, for example, comprise an axially compressible polymeric material, such as a longitudinally extruded and expanded polymer, including expanded polytetrafluoroethylene (“ePTFE”), expanded modified PTFE, expanded copolymers of PTFE, nylons, polycarbonates, polyethylenes, polypropylenes, polyurethanes and the like. In various embodiments, polymeric tubular member 102 comprises an extruded ePTFE tube, such as the tubes described in U.S. Pat. Nos. 3,953,566 and 4,187,390. In other embodiments, polymeric tubular member 102 comprises a wrapped ePTFE film tube. For example, member 102 can comprise a tube made from an ePTFE film that has been cigarette wrapped on the surface of a mandrel or, alternatively, has been helically wrapped on the surface of a mandrel. Such ePTFE films of this type can be made generally as taught by U.S. Pat. Nos. 3,953,566 and 4,187,390. In yet other embodiments, member 102 can comprise a polymeric open celled material. However, any suitable polymeric tubular member is within the scope of the present disclosure.

In various embodiments, polymeric tubular member 102 comprises an ePTFE tube having microstructure of nodes interconnected by fibrils. The microstructure of polymeric tubular member 102 can comprise a multiplicity of fibrils having a mean fibril length. Mean fibril length can be determined, for example, by examining a photomicrograph of the surface of polymeric tubular member 102 and by taking the mean of ten measurements made in the predominant direction of the fibrils between nodes connected by fibrils. First, a photomicrograph is made of a representative region of the sample surface, of adequate magnification to show at least five sequential fibrils within the length of the photomicrograph. A series of five measurements are taken along a straight line drawn onto the surface of the photomicrograph in the predominant direction of the fibrils followed by a second series of five measurements made along a second line drawn parallel to the first. A measurement constitutes the distance between adjacent nodes connected by at least one fibril. The ten measurements obtained by this method are averaged to obtain the mean fibril length of the region.

For example, as illustrated in FIG. 2, any or all of length portions 102, 108, and 106 can have a multiplicity of bent fibrils 214.

Tapered length portion 108 can, for example, possess a rapid recovery property, i.e., a spring-like property. Rapid recovery as herein defined is the difference between the extended length of a material and the recovered length with respect to the recovered length, as generally described in U.S. Pat. No. 5,026,513. The extended length is the length of material under tensile load and recovered length is the length of material. In various embodiments, rapid recovery can be quantified by the following equation:

RR %=(l _(t) −l _(r))×100%

(l _(r))

where l_(t) is the length of the tapered length portion 108 when extended axially under 1 maximum tensile force, and l_(r) is the length of the tapered portion five seconds after the release of the tensile force. Tapered length portion 108 having rapid recovery properties can, for example, exhibit improved bending characteristics and improved resistance to kinking, constriction, and/or collapse under bending.

In various embodiments, tapered length portion 108 can comprise a uniform frustoconical section. In such embodiments, tapered length portion 108 expands in the manner of a uniform frustoconical section from a diameter of first smaller diameter length portion 104 to a diameter of second larger diameter length portion 106.

In other embodiments, tapered length portion 108 comprises a non-uniform shape. For example, tapered length portion 108 can expand from a diameter of first smaller diameter length portion 104 to a diameter of second larger diameter length portion 106 in a non-uniform manner, such as a curved, non-linear shape. Any shape of tapered length portion 108 is within the scope of the present disclosure.

A method for making a tapered implantable device of the present disclosure is described as follows. A polymeric tubular member is fitted over a first mandrel having first, longer tapered length segment to form a first tapered length portion along a portion of the length of the polymeric tubular member. The polymeric tubular member is removed from the first mandrel and fitted over and axially compressed onto a second mandrel having a second, shorter tapered length segment to form the first tapered length portion into a second tapered length portion. A female die can optionally be used assist in compression of the polymeric tubular member on the second mandrel, particularly over the second tapered length portion. The polymeric tubular member can then be removed from the second mandrel.

FIGS. 3A and 3B illustrate an example step in a method to form a tapered implantable implant. Polymeric tubular member 102 is fitted over a first mandrel 330. First mandrel 330, as shown in FIG. 3A, comprises a smaller diameter length segment 334, a larger diameter length segment 336, and a first, longer tapered length segment 338. First, longer tapered length segment 338 is typically located between smaller diameter length segment 334 and larger diameter length segment 336.

In various embodiments, polymeric tubular element 102 initially comprises a diameter (consistent along its length) equal to or slightly less than the diameter of smaller diameter length segment 334. Polymeric tubular member 102 is placed around the exterior surface of first mandrel 330 and pulled onto the mandrel in the direction of the first larger diameter length segment 336. In various embodiments, as polymeric tubular member 102 is fitted over first mandrel 330 it is stretched over first, longer tapered length segment 338 to larger diameter length segment 336, forming second larger diameter length portion 106 and tapered portion having a first longer length 318.

In various embodiments, the respective lengths of larger diameter length portion 104 and smaller diameter length portion 106 can be selected to position tapered portion having a first longer length 318 at a desired position onto polymeric tubular member 102. For example, a tapered implantable device having a particular length of a larger diameter and particular length of a shorter diameter may be desired. It can also be appreciated that the tapered implantable device may be continuously tapered between the opposing ends of the device. By providing a method for placing a tapered portion having a multiplicity of bent fibrils between a smaller diameter length portion 104 and a larger diameter length portion 106, a tapered implantable device 100 having at least sufficient length of smaller diameter length portion 104 and larger diameter length portion 106 can be formed. In such embodiments, tapered implantable device 100 can be sized by, for example, cutting one or both ends of polymeric tubular member 102 such that a sufficient length of smaller diameter length portion 104 and larger diameter length portion 106 is provided.

Prior to removal of polymeric tubular member 102 from first mandrel 330, member 102 can be exposed to further processing steps. For example, polymeric tubular member 102 can be wrapped with a biocompatible reinforcing film, such as an ePTFE film. Any biocompatible material capable of reinforcing polymeric tubular member 102 is within the scope of the present disclosure.

For example, a length portion of polymeric tubular member 102, such as tapered length portion with a first longer length 318, can be heated. Further, heat can be applied to the entire first mandrel 330 and polymeric tubular member 102. Any processing of polymeric tubular member 102, including tapered length portion having a first longer length 318, is within the scope of the present disclosure.

In various embodiments, the outer surface of porous tubular member 102 can be coated with an elastomer. For example, as referenced in U.S. Pat. No. 8,029,563, a silicone composition such as MED-1137 Adhesive Silicone Type A from NuSil Silicone Technology (Carpenteria, Calif.) can be applied to the outer surface of porous tubular member 102. In various embodiments, the elastomer is applied after porous tubular member 102 is heated. Any application of elastomer to porous tubular member 102 is within the scope of the present disclosure.

Further, prior to removal from first mandrel 330, porous tubular member 102 can be surrounded by an optional second porous tubular member. In various embodiments, the optional second porous tubular member comprises a larger inner diameter than an outer diameter of the porous tubular member 102. The optional second porous tubular member can be positioned concentrically around first tubular member 102 on mandrel 330.

As illustrated in FIG. 4A, a second mandrel 440 can comprise a larger diameter length segment 446, a smaller diameter length segment 444, and a second, shorter tapered length segment 448. Second, shorter tapered length segment 448 is typically located between smaller diameter length segment 444 and larger diameter length segment 446.

With reference to FIG. 4B, polymeric tubular member 102 having a tapered portion with a first longer length 318 can be fitted over second tubular mandrel 440 such that tapered length portion 318 is located at or near second, shorter tapered length segment 448. Polymeric tubular member 102 can then be compressed longitudinally along second mandrel 440 in the direction of a larger diameter length segment 446, which converts tapered portion having a first longer length 318 to a tapered portion having a second shorter length 108. In such embodiments, shorter diameter length portion 104 and longer diameter length portion 106 of polymeric tubular member 102 do not experience a significant length change, as only tapered portion having a first longer length 318 is compressed against an exterior surface of second mandrel 440. As such, as previously described, the desired dimensions of tapered implantable device 100 can be selected prior to formation of tapered portion having a second shorter length 108.

A compression ratio can be used to describe the amount of longitudinal compression applied to tapered portion having a first longer length 318. For example, a compression ratio can comprise a ratio of the length tapered portion having a second shorter length 108 to the length of tapered portion having a first longer length 318. In various embodiments, the compression ratio can be between about 75% and 95%. In other embodiments, the compression ratio can be between about 50% and 75%. In yet other embodiments, the compression ratio can be between about 25% and 50%. The compression ratio may range as low as about 15%, and is largely dependent on the bulk density of the chosen porous precursor material.

In various embodiments, the compression ratio can correlate with the respective lengths of tapered portion having a second shorter length 108 and tapered portion having a first longer length 318. For example, a mandrel ratio can comprise the ratio of the length of second, shorter tapered length segment 448 to the length of first, longer tapered length segment 338. Preferably, the compression ratio and the mandrel ratio are substantially the same. In other embodiments, the mandrel ratio is within 10% of the compression ratio. In yet other embodiments, the mandrel ratio is within 33% of the compression ratio. Any correlation between the compression ratio and the mandrel ratio is within the scope of the present disclosure.

In various embodiments, as illustrated in FIG. 4C, a female die 450 can be used to assist in formation of tapered portion having a second shorter length 108. For example, female die 450 can apply a longitudinally compressive force against polymeric tubular member 102 at or near second, shorter tapered length segment 448, causing tapered portion having a first longer length 318 to compress against second, shorter tapered length segment 448 of second mandrel 440. Female die 450 can comprise, for example, a complementary shape to second, shorter tapered length segment 448 of second mandrel 440. In other embodiments, female die 450 comprises a shape different from that of second, shorter tapered length segment 448. In such embodiments, female die 450 can assist in providing a desired shape on an external surface of polymeric tubular member 102, including tapered portion having a second shorter length 108.

Further, female die 450 can assist in providing a consistent thickness of polymeric tubular member 102 in the smaller diameter region 104 and/or the tapered portion having a second shorter length 108. Any configuration of female die 450 that assists in forming tapered portion having a second shorter length 108 in a porous tubular member is within the scope of the present disclosure.

Prior to removal of polymeric tubular member 102 from second mandrel 440, member 102 can be exposed to further processing steps. For example, a portion of polymeric tubular member 102, such as tapered portion with a second shorter length 108, can be heated. Further, heat can be applied to the entire second mandrel 440 and polymeric tubular member 102. Any processing of polymeric tubular member 102, including tapered portion having a second shorter length 108, is within the scope of the present disclosure.

After formation of tapered portion having a second shorter length 108, tapered implantable device 100 can be removed from second mandrel 440 and prepared for use in the anatomy of a patient. In various embodiments, tapered implantable device 100 can be combined with a medical device such as, for example, a stent. In other embodiments, tapered implantable device 100 can be used without combination with another medical device. In such embodiments, tapered implantable device 100 can comprise a graft. Although described in particular embodiments, tapered implantable device 100 can be used alone or in combination with any suitable medical device for implantation within the anatomy of a patient.

Several characteristics and advantages have been set forth in the preceding description, including various alternatives together with details of the structure and function of the devices and methods. The disclosure is intended as illustrative only and as such is not intended to be exhaustive or limiting. It will be evident to those skilled in the art that various modifications may be made, especially in matters of structure, materials, elements, components, shapes, sizes, and arrangements of parts including combinations within the principles described herein, to the full extent indicated by the broad, general meaning of the terms in which the appended claims are expressed. To the extent that these various modifications depart from the spirit and scope of the appended claims, they are intended to be encompassed therein. 

What is claimed is:
 1. An implantable article comprising: a polymeric tube comprising a first length portion having a first diameter and a second length portion having a second diameter, the first length having a first rapid recovery property defined by a difference between an extended length of the first length portion and a recovered length of the first length portion; and a tapered length portion extending between the first length portion and the second length portion, the tapered length portion having a tapered length portion rapid recovery property that is defined by a difference between an extended length of the tapered length portion and a recovered length of the tapered length portion, wherein the first rapid recovery property differs from the tapered length rapid recovery property at a compression ratio between 30% and 95%.
 2. The implantable article of claim 1, wherein the tapered length portion rapid recovery property is greater than the first rapid recover property.
 3. The implantable article of claim 1, wherein the polymeric tube is formed of expanded polytetrafluoroethylene.
 4. The implantable article of claim 1, wherein the tapered length portion defines a non-uniform shape.
 5. The implantable article of claim 1, wherein the tapered portion defines a uniform, frustoconical shape.
 6. The implantable article of claim 1, wherein the first diameter is smaller than the second diameter.
 7. The implantable article of claim 1, wherein the tapered length portion has an expanded polymeric microstructure.
 8. The implantable article of claim 7, wherein the tapered length portion includes a multiplicity of fibrils, the majority of which are bent fibrils.
 9. The implantable article of claim 1, wherein the compression ratio is between about 50% to 75%.
 10. An implantable article comprising: a polymeric tube comprising a first portion having a first diameter and a second portion having a second diameter, the first diameter being less than the second diameter, and the first length having a first rapid recovery property defined by a difference between an extended length of the first length portion and a recovered length of the first length portion; and a tapered portion extending between the first portion and the second portion, the tapered portion having a tapered portion rapid recovery property that is defined by a difference between an extended length of the tapered portion and a recovered length of the tapered portion, wherein the tapered portion rapid recovery property defines a compression ratio of between 30% and 95%.
 11. The implantable article of claim 10, wherein the tapered length portion rapid recovery property is greater than the first rapid recovery property.
 12. The implantable article of claim 10, wherein the polymeric tube is formed of expanded polytetrafluoroethylene.
 13. The implantable article of claim 10, wherein the tapered length portion defines a non-uniform shape.
 14. The implantable article of claim 10, wherein the tapered portion defines a uniform, frustoconical shape.
 15. A method of manufacturing an implantable article having a tapered length portion extending between a first length portion and a second length portion, the method comprising: forming a tapered length portion having a first length in a polymeric tube using a first mandrel having a first tapered length segment; removing the polymeric tube from the first mandrel; compressing the tapered portion having the first length of the polymeric tube on a second mandrel having a second tapered length segment such that the tapered portion has a second length that is shorter than the first length; and removing the polymeric tube from the second mandrel.
 16. The method of claim 15, wherein a compression ratio is defined by the ratio of the tapered portion having a first length to the tapered portion having a second length, a mandrel ratio is defined by a ratio of a length of the first tapered length segment to a length of the second tapered length segment, and wherein the mandrel ratio has a value within 33% of the compression ratio.
 17. The method of claim 16, wherein the compression ratio is between 30% and 95%.
 18. The method of claim 16, wherein the compression ratio is approximately equal to the mandrel ratio.
 19. The method of claim 15, wherein the method further includes heating the polymeric tube after compressing the tapered portion of the polymeric tube on the second mandrel.
 20. The method of claim 15, wherein prior to removing the polymeric tube from the first mandrel, the method further includes wrapping the polymeric tube with a reinforcing member. 